minute.
| Substrat e | Application Surface | Adhesion Promoter | ||
| Substrat e | Application Surface | NO ADHESION PROMOTER lb./in. (N/25mm) | WP-2000 (water-based) lb./in. (N/25mm) | 3M™ Tape Primer94 (solvent-based)lb./in. (N/25mm) |
| Wood | MDF (w/ sealer) | 2 (8)3 | 11 (51) | 4 (18) |
| Wood | Painted MDF | 4 (20) | 12 (52) | 7 (31) |
| Boards | Gypsum Board (w/skim coat & sealer) | 2 (8)3 | 8 (35) | 4 (19) |
| Metals | Aluminum | 11 (47) | 11 (48) | 11 (47) |
| Metals | Anodized Aluminum | 5 (23) | 13 (56) | 11 (49) |
| Metals | Stainless Steel | 6 (26) | 13 (56) | 6 (28) |
| Glass | Glass | 6 (26) | 13 (58) | 6 (26) |
| Plastics1 | ABS | 6 (28) | 13 (56) | 10 (44) |
| Plastics1 | Acrylic | 5 (22) | 12 (54) | 10 (43) |
| Plastics1 | Polyester (PETG) | 7 (29) | 11 (51) | 10 (45) |
| Plastics1 | Polypropylene | 1 (2) | 4 (17) | 4 (20) |
| Plastics1 | Polyethylene | 1 (3) | 5 (21) | 1 (3) |
| Plastics1 | Polycarbonate | 6 (28) | 12 (53) | 10 (44) |
| Plastics1 | DI-NOC™ Film | 5 (24)2 | 11 (49) | 9 (42) |
WP-2000 undiluted for testing
|
Characteristic |
Evaluation |
Results |
Dimensional Stability* |
4 in. x 4 in. (100mm x 100mm) crosscut in film, after 2 days at room temperature. |
Largest gap: < 0.01 in. (0.3mm) |
|
Heat Resistance* |
Aged at 150°F (65°C) for 28 days. |
No delamination or visible change |
|
Thermal Cycle Resistance* |
Cycled between -22°F and 150°F (-30°C and 65°C) for 12 days. |
No delamination or visible change |
Moisture Resistance* |
Aged at 104°F (40°C), 95% humidity for 30 days. |
No delamination or visible change |
Cold Impact Resistance* |
2 lb. (907g) weight dropped from 5 in. (12.7cm) height, at 32°F (0°C) using a Gardner Impact Tester. |
No cracks in film |
|
Ultraviolet Light Exposure |
Exposed to carbon arc accelerated UV light for 250 hours |
No visible change |
Abrasion Resistance |
Taber® CS-17 Abrasion wheel: 1 Kg loading weight, 7,000 cycles |
No wear-through of surface finish |
Fire Resistance |
When used in Interior Applications as defined by NFPA 101 “Life Safety Code”, Test Method ASTM E84 |
Most Products have Class A |
Industry-Specific Testing |
IMO Certification/USCG Type Approval, Intertek Firedoor, and CAN/ULC-S102.2 |
Consult 3M Tech- nical Service |
Substrat e |
Application Surface |
Adhesion Promoter |
||
|
NO ADHESION PROMOTER lb./in. (N/ 25mm) |
WP-2000 (water-based) lb./in. (N/ 25mm) |
3M™ Tape Primer 94 (solvent- based) lb./in. (N/25mm) |
||
Wood |
MDF (w/ sealer) |
2 (8)3 |
11 (51) |
4 (18) |
|
Painted MDF |
4 (20) |
12 (52) |
7 (31) |
|
Boards |
Gypsum Board (w/ skim coat & sealer) |
2 (8)3 |
8 (35) |
4 (19) |
Metals |
Aluminum |
11 (47) |
11 (48) |
11 (47) |
|
Anodized Aluminum |
5 (23) |
13 (56) |
11 (49) |
|
|
Stainless Steel |
6 (26) |
13 (56) |
6 (28) |
|
|
Glass |
Glass |
6 (26) |
13 (58) |
6 (26) |
Plastics1 |
ABS |
6 (28) |
13 (56) |
10 (44) |
|
Acrylic |
5 (22) |
12 (54) |
10 (43) |
|
|
Polyester (PETG) |
7 (29) |
11 (51) |
10 (45) |
|
|
Polypropylene |
1 (2) |
4 (17) |
4 (20) |
|
|
Polyethylene |
1 (3) |
5 (21) |
1 (3) |
|
|
Polycarbonate |
6 (28) |
12 (53) |
10 (44) |
|
|
DI-NOC™ Film |
5 (24)2 |
11 (49) |
9 (42) |
|
Product Series |
Texture of Applicatio n Surface1 |
Damage to Film Surface2 |
Printed/ Embossed Pattern Match at Double- cut Seams3 |
Reflection of Pattern at Double-cut Seams4 |
Lighting Environment After Application5 |
Not Recommended On Compound Curved Surfaces6 |
Notes |
BW Entertainment |
• Do not crease or dent the film during application. • Not recommended for com- pound curved surfaces due to distortion of textured surface. |
||||||
LE Leather |
LE-1226, LE-1227, LE-1228, LE-1229, LE-1230, LE-1231 LE-1551 LE-1552 |
LE-1171 |
LE-1171 |
LE-1552 |
• For LE-1552 only: not recom- mended for compound curved surfaces due to distortion of textured surface. |
||